材料成型工艺基础部分
0 绪论
金属材料：metal material (MR)
高分子材料：high-molecular material
陶瓷材料：ceramic material
复合材料：composition material
成形工艺：formation technology
1 铸造
铸造工艺：casting technique
铸件：foundry goods （casting）
机器零件：machine part
毛坯：blank
力学性能：mechanical property
砂型铸造：depositionsand casting process
型砂：foundry sand
1.1 铸件成形理论基础
合金：alloy
铸造性能：casting property
工艺性能：processing property
收缩性：constringency
偏析性：aliquation
氧化性：oxidizability
吸气性：inspiratory
铸件结构：casting structure
使用性能：service performance
浇不足：misrun
冷隔：cold shut
夹渣：cinder inclusion
粘砂：sand fusion
缺陷：flaw, defect, falling
流动性：flowing power
铸型：cast (foundry mold)
蓄热系数：thermal storage capacity
浇注：pouring
凝固：freezing
收缩性：constringency
逐层凝固：layer-by-layer freezing
糊状凝固：mushy freezing
结晶：crystal
缩孔：shrinkage void
缩松：shrinkage porosity
顺序凝固：progressive solidification
冷铁：iron chill
补缩：feeding
等温线法：constant temperature line method
内接圆法：inscribed circle method
铸造应力：casting stress
变形：deforming
裂纹：crack
机械应力：mechanical stress
热应力：heat stress
相变应力：transformation stress
气孔：blow hole
铸铁：ingot
铸钢：cast steel
非铁合金：nonferrous alloy
灰铸铁：gray cast-iorn
孕育处理：inoculation
球墨铸铁：spheroidal
球化处理：sheroidisation
可锻铸铁：ductile cast iron
石墨：graphite
蠕墨铸铁：vermicular cast iron
热处理：heat processing
铝合金：Al-alloy
熔炼：fusion metallurgy
铜合金：copper alloy
氢脆：hydrogen brittleness
1.2 铸造方法 （casting method）
手工造型：hand moulding
机器造型：machine moulding
金属型：metal mold casting
金属模：permanent mould
压力铸造：press casting
熔模铸造：investment moulding
蜡膜：cere
离心铸造：centrifugal casting
低压铸造：casting under low pressure
差压铸造：counter-pressure casting
陶瓷型铸造：shaw process
1.3 铸造工艺设计
浇注位置：pouring position
分型面：mould joint
活块：loose piece
起模：patter drawing
型芯：core
型芯撑：chaplet
工艺参数：processing parameter
下芯：core setting
合型：mould assembly